Composite – prevest fusion core

Light curing for time saving application
Additional chemical curing for complete polymerisation
Low heat development even in bulk application
Flowable, non slumping formula for convenient placement
Low shrinkage properties

Technical Data:

1) Working Time : 60 sec.
2) Setting Time : 3 – 4 min.
3) Compressive Strength : 140 – 150 MPa.
4) Flexural Strength : 60 – 70 MPa.
5) Film Thickness : 50 µm

Composition :

Base Paste : Bisphenol A Glycidyle Methacrylate, Ethoxylated Bisphenol A Dimethacrylate, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agents and Stabilizers.

Catalyst Paste : Bisphenol A Glycidyle Methacrylate, Ethoxyated Bisphenol A Dimethacrylate, Ethoxlated, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agents and Stabilizers

Cautions : Use of zinc oxide, eugenol containing materials must be avoided.

Storage Conditions : Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life not affected after opening if stored in a cool dry place.

Shelf Life : 2 years from the date of manufacturing.

Sufficiently dry the working area.
Prepare the cavity suitably for the restorative treatment and should be minimally invasive in order to protect healthy dental hard tissue.
Clean and dry the cavity.
Protect the pulp suitably with a light cure cavity liner preferably with Cal LC or Fusion I-Seal.
Apply Fusion Bond DC to the prepared cavity.
Remove the cartridge cap and attach a mixing tip.
Attach intra oral tip if required.
Place matrix around the prepared tooth and apply Fusion Core DC Flo directly from the cartridge.
Allow 3-4 minutes for the material to set properly.
Light cure for 40 sec.
Restoration can be finished immediately after light curing.